Fiberglass Stitched Mat

Fiberglass stitched mat is made of chopped fiberglass strands in a certain length, then freely put and stitched together with polyester tissue or carbon fiber tissue by polyester yarn. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in pultrusion pipes and tanks, FRP boat, insulation panels, anode tubes, auto parts, bath tubes etc, suitable for pultrusion, filament winding, RTM, hand lay-up processes.

General Data

Instructions for Use and Storage Conditions

Roll width: Standard width in 1200mm, 1270mm, and other sizes depends on customer's real needs, available in 200mm to 3200mm.

Packing: Fiberglass stitched mat is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.

Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.

Single Warp Fiberglass Fabric

Single warp fiberglass fabric is made of fiberglass direct roving parallel aligned in 0°directions, then stitched by polyester yarn. Also can select to add chopped strand layer or non-woven fabric layer stitched together. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in wind energy, boat building, FRP pipes and tanks, pultrusion section industry etc, suitable for pultrusion, hand lay up, filament winding, vacuum infusion processes.

General Data

Instructions for Use and Storage Conditions

Roll width: Standard width in 1270mm, and other sizes depends on customer's real needs, available in 200mm to 2600mm.

Packing: Single warp fiberglass fabric is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.

Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.

Fiberglass Stitch Bonded Fabric

Fiberglass stitch bonded fabric is made of fiberglass direct roving parallel aligned in 0°and 90°directions, then stitched together with chopped strand layer or polyester tissue layer as combo mat. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in boat building, wind energy, automotive, sports equipment, flat panels etc, suitable Vacuum infusion, hand lay-up, pultrusion, RTM forming processes.

General Data

Instructions for Use and Storage Conditions

Roll width: Standard width in 1200mm, 1270mm, and other sizes depends on customer's real needs, available in 200mm to 2600mm.

Packing: Fiberglass stitch bonded fabric is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.

Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.

Fiberglass Double Biaxial Fabric

Fiberglass double biaxial fabric is made of fiberglass direct roving parallel aligned in +45°and -45°directions, then stitched together with or without chopped strand layer as combo mat. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in boat building, wind energy, automotive, sports equipment, containers etc, suitable Vacuum infusion, hand lay-up, pultrusion, RTM forming processes.

General Data

Instructions for Use and Storage Conditions

Roll width: Standard width in 1250mm, 1270mm, and other sizes depends on customer's real needs, available in 200mm to2600mm.

Packing: Fiberglass double biaxial fabric is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.

Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.

Multiaxial core mat

Multiaxial core mat is made of biaxial fabric (0°and 90°) combined middle layer PP, PET or Nylon core material and plus the chopped strands layer, then stitched together like sandwich design. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in boat building, wind energy, automotive, train parts, storage tanks etc, suitable for RTM, Vacuum infusion, hand lay-up forming processes.

General Data

Instructions for Use and Storage Conditions

Roll width: Standard width in 1270mm, and other sizes depends on customer's real needs, available in 200mm to 2600mm.

Packing: Fiberglass multiaxial core mat is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.

Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.

Fiberglass Triaxial Fabric

Fiberglass triaxial fabric is made of fiberglass direct roving parallel aligned in 0°, +45°, -45°or +45°, 90°, -45°directions, then stitched together with or without chopped strand layer as combo mat. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in boat building, wind energy, automotive, sports equipment, containers etc, suitable Vacuum infusion, hand lay-up, pultrusion, RTM forming processes.

General Data

Instructions for Use and Storage Conditions

Roll width: Standard width in1250mm, 1270mm, and other sizes depends on customer's real needs, available in 200mm to2600mm.

Packing: Fiberglass triaxial fabric is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.

Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.

Woven Roving Combo Mat

Woven roving combo mat is made of woven roving and chopped fiberglass strand complex of, then stitched together with polyester yarn. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in boat building, Auto parts, refrigerated tools and structural sections industry etc, suitable for hand lay up, RTM, pultrusion, vacuum processes.

General Data

Instructions for Use and Storage Conditions

Roll width: Standard width in 1250mm, 1270mm, and other sizes depends on customer’s real needs, available in 200mm to 2600mm.

Packing: Fiberglass woven roving combo mat is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.

Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.

E-Glassfiber ST Woven

E-glassfiber ST woven is characterized by flame-retardant, corrosion & heat resisrant, high strength and insulation, etc. It is widely used in chemical industry .shipping , automobile .architecture, etc. Because it has special property such as hear-resistant,fire-proof and impact-resistant, so it is widly used in helmet and pine line. According to sizing it is no-paraffin. It can be consistented with multi-resin system, such as UP, Vinyl resin , Epoxy resin etc.

Specifications

1. According to standard JC/T170-1996.
2. Welcome to make demands on other specifications.
3. The highest softening temperature is 550-750eC