Powder & Emulsion Fiberglass Chopped Strand Mat

Setting the global standard for general-purpose composites, POLYMER is a premier fast wet-out chopped strand mat supplier and manufacturing source. Our premium powder emulsion fiberglass chopped strand mat is meticulously crafted from evenly distributed E-glass strands, offering fabricators the precise choice between high-solubility powder or strong-binding emulsion formats.

Engineered as a fully UP VE Epoxy compatible fiberglass mat, this highly versatile substrate guarantees rapid resin impregnation and exceptional mold conformability without frustrating spring-back. It serves as the ultimate structural reinforcement for hand lay-up and press molding processes, delivering heavy-duty multi-directional strength to marine boat hulls, automotive panels, and anti-corrosion cooling towers.

Ultra-Fast Resin Wet-Out

Superior Mold Conformability

Multi-Directional Strength

UP/VE/Epoxy Compatible

Zero Spring-Back Layup

Model:PLM100

WhatsApp Now

Chopped Strand Mat

Chopped strand mat is made of fiberglass chopped strands bonded with powder or emulsion binder uniformly. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in boat building, automotive, cooling towers, bathroom accessories, anti-corrosion pipes etc, suitable for hand lay up, filament winding, press molding forming processes.

Core Performance Advantages

Rapid Wet-Out & Excellent Compatibility

Bonded with premium powder or emulsion binders, the mat ensures extremely fast and uniform wet-out. It is highly compatible with Polyester, Vinyl Ester, and Epoxy resins, reducing resin consumption and accelerating production cycles.

Superior Uniformity & High Tensile Strength

Manufactured with precisely distributed fiberglass chopped strands, it delivers outstanding multi-directional mechanical properties. With tensile strength reaching up to 150N, it guarantees the structural integrity of heavy-duty FRP composites.

Exceptional Mold Conformability

Featuring excellent flexibility and wet strength retention, the mat easily conforms to complex and intricate mold shapes. This makes it the ideal reinforcement substrate for demanding hand lay-up and press molding forming processes.

Versatile Industrial Applications

Available in a wide weight range (100g to 600g/m²), it perfectly meets the diverse specifications required for boat building, automotive manufacturing, cooling towers, bathroom accessories, and anti-corrosion filament winding pipes.

General Data

Code	Weight (g/m2)	Binder type	L.O.I	Moisture content	T. Strength (N)
Code	Weight (g/m2)	Binder type	L.O.I	Moisture content	Vertical	Horizontal
PLM100	100	Powder/Emulsion	4.0-12.0	≤0.2	≥80	≥80
PLM120	120	Powder/Emulsion	4.0-12.0	≤0.2	≥80	≥80
PLM150	150	Powder/Emulsion	4.0-12.0	≤0.2	≥100	≥100
PLM200	200	Powder/Emulsion	4.0-12.0	≤0.2	≥100	≥100
PLM225	225	Powder/Emulsion	2.0-8.0	≤0.2	≥100	≥100
PLM300	300	Powder/Emulsion	2.0-8.0	≤0.2	≥120	≥120
PLM380	380	Powder/Emulsion	2.0-8.0	≤0.2	≥120	≥120
PLM450	450	Powder/Emulsion	2.0-8.0	≤0.2	≥150	≥150
PLM600	600	Powder/Emulsion	2.0-8.0	≤0.2	≥150	≥150

Instructions for Use and Storage Conditions

Roll width: Standard width in 1040mm, 1270mm, and other sizes depends on customer’s real needs, available in 200mm to 3200mm.

Packing: Fiberglass chopped strand mat is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.

Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.